directglazing

DIRECT GLAZING ADHESIVES

  • 207plus
    Polyurethane direct glazing adhesive sealant

    U-SEAL 207 Plus is an excellent non-sag, one-component, flexible and high performance polyurethane adhesive sealant for direct glazing of windshield and bonding of front, side and rear glass used in commercial/industrial vehicles. Suitable for elastic structural bonding (assembly of various materials which are subjected to high thermal and dynamic stress) in the transportation industry.

    • One-component solvent free po dvvlyurethane
    • Non-sag, with minimal stringing
    • Low-conductivity. Suitable for use with integrated antenna
    • Prevents corrosion in aluminium-body vehicles.
  • • Colours Black
    • Curing rate (1 day at 23°C and 50% r.h.) 3 mm/24h
    • Shore A (23°C and 50% r.h.) 55
    • Tack-Free Time (23°C and 50% r.h.)
    35'
    • Tensile strength (ISO 37 DIN 53504) ≥ 7,5 N/mm2
    • Elongation (ISO 37 DIN 53504) ≥ 500 %
    • Application Temperature from +5 to +40 (°C)
    • Temperature Resistance (after curing) -40 / +100 (°Ccs

    Packaging
    310 ml cartridge; 400/600 ml sausage;
     
  • DRIVE AWAY TIME: 3 hours on vehicles fitted with both driver & passenger airbags.
     

    207plus 001    207plus 002 

  • 201fast
    Fast curing polyurethane direct glazing adhesive sealant

    U-SEAL 201 Fast is a fast curing, flexible and high performance one-component polyurethane adhesive sealant for direct glazing. It is specifically designed to give a fast and safe drive-away time on vehicles fitted with airbags. Particularly fast skinning and curing time. Purposely designed for bonding windscreens, side and rear windows of passenger cars, trucks, tractors and special vehicles, is also used for bonding fibreglass reinforced plastic elements (roof, side and frontal panels).

    • Rapid application and curing
    • One-component solvent free polyurethane.
    • Non-sag, with minimal stringing
    • Low-conductivity. Suitable for use with integrated antenna
    • Prevents corrosion in aluminium-body vehicles.
  • • Colours Black
    • Curing rate (1 day at 23°C and 50% r.h.) 4 mm/24h
    • Shore A (23°C and 50% r.h.) 55
    • Tack-Free Time (23°C and 50% r.h.)
    15'
    • Tensile strength (ISO 37 DIN 53504)
    ≥ 9 N/mm2
    • Elongation (ISO 37 DIN 53504) ≥ 300 %
    • Application Temperature from +5 to +40 (°C)
    • Temperature Resistance (after curing) -40 / +100 (°C)

    Packaging
    310 ml cartridge; 400/600 ml sausage;
     
  • DRIVE AWAY TIME: 2 hours on vehicles fitted with both driver & passenger airbags.
     

    201fast 001    201fast 002    201fast 003

  • 205hm
    Ultra-fast, High Modulus & Low Conductivity polyurethane direct glazing adhesive sealant.

    U-SEAL 205 HM-LC is a ultra-fast curing, flexible and high performance one-component polyurethane adhesive sealant for the direct glazing of vehicle glass. It is ideal for bonding on vehicles where high shear modulus and non-conductive properties are required. It combines high modulus rigidity, very low volume resistivity and good high-frequency properties, allowing the correct bonding of glass with integrated antenna or additional electrical equipment.

    • Rapid application and curing
    • One-component solvent free polyurethane.
    • Capable of withstanding high dynamic stresses
    • Non-sag, with minimal stringing
    • Low-conductivity. Suitable for use with integrated antenna
  • • Colours Black
    • Curing rate (1 day at 23°C and 50% r.h.) 4 mm/24h
    • Shore A (23°C and 50% r.h.) 60
    • Tack-Free Time (23°C and 50% r.h.)
    15'
    • Tensile strength (ISO 37 DIN 53504)
    ≥ 9 N/mm2
    • Elongation (ISO 37 DIN 53504) ≥ 300 %
    • Application Temperature from +5 to +40 (°C)
    • Temperature Resistance (after curing) -40 / +100 (°C)

    Packaging
    310 ml cartridge; 400/600 ml sausage;
     
  • DRIVE AWAY TIME: 1 hours on vehicles fitted with both driver & passenger airbags.
     

    205 001            205 002

  • 208btr
    High viscosity polyurethane direct glazing adhesive sealant. Specific for bonding and sealing in BTR.

    U-SEAL 208 BTR is an excellent high viscosity, one-component, flexible and high performance polyurethane adhesive sealant for the direct glazing of windshield and front, side and rear glass in the Bus, Truck and Railway industry. With its high resistance to UV, weathering and ageing it is designed for the sealing of exposed joints, including joints between lateral glass.

    • One-component polyurethane, solvent free.
    • Non-sag, with minimal stringing
    • High Viscosity and Green strength
    • High UV, weathering and ageing resistance
  • • Colours Black
    • Curing rate (1 day at 23°C and 50% r.h.) 3 mm/24h
    • Shore A (23°C and 50% r.h.) 60
    • Tack-Free Time (23°C and 50% r.h.)
    30' - 40'
    • Tensile strength (ISO 37 DIN 53504)
    ≥ 10 N/mm2
    • Elongation (ISO 37 DIN 53504) ≥ 600
    • Application Temperature from +5 to +40 (°C)
    • Temperature Resistance (after curing) -40 / +100 (°C)

    Packaging
    400/600 ml sausage;
     
  • DRIVE AWAY TIME: 1 hours on vehicles fitted with both driver & passenger airbags.
     

    208 001            208 002

  • simpseal60hv
    Primerless, high green stregth and fast curing hybrid polymer direct glazing adhesive sealant.
    SiMP®-SEAL 60 HV is a fast curing, flexible and high performance one-component Silyl-terminated polymer (SiMP®) adhesive sealant for the primerless direct glazing of vehicle glass. It is suitable for the bonding of windshields and side or rear windows of cars, buses, trucks, cabins and special vehicles. Ideal for the bonding of fibreglass reinforced plastic elements (roof, side and frontal panels) to structures.
    • Primerless adhesion
    • Rapid application and curing
    • One-component isocyanate solvent free Silyl-terminated polymer (SiMP®).
    • Non sag, with short cut-off string. High green strength
    • Low-conductivity. Suitable for use with integrated antenna
    • Prevents corrosion in aluminium-body vehicle.
  • • Colours Black
    • Curing rate (1 day at 23°C and 50% r.h.) 3,5 mm/24h
    • Shore A (23°C and 50% r.h.) 60
    • Tack-Free Time (23°C and 50% r.h.)
    15'
    • Tensile strength (ISO 37 DIN 53504)
    ≥ 3,9 N/mm2
    • Elongation (ISO 37 DIN 53504) ≥ 350 %
    • Application Temperature from +5 to +40 (°C)
    • Temperature Resistance (after curing) -40 / +100 (°C)

    Packaging
    290 ml cartridge; 400/600 ml sausage; 200 lt drum;
     
  • DRIVE AWAY TIME: 1 hours on vehicles fitted with both driver & passenger airbags.
     

    simpseal60hv 001    simpseal60hv 002    simpseal60hv 003

    Certificates and compliances:
    FMVSS 212 Certified
    Euro-NCAP frontal impact sled condition conform
    (European New Car Assessment Programme)

  • u-activator
    Glass activator and cleaner
    U-Activator is a silane polymer-based surface cleaner and activator able to remove the contamination of the glass. Its chemical nature also enhances the adhesion promotion properties of U-Primer 130 and the adhesive during the glass replacement contributing to the perfect bonding of the glass. U-Activator is very moisture sensitive. Close the containers immediately after every use to preserve contents.
  • • Colours Transparent
    • Solid content 35 %
    • Drying time (23°C and 50% r.h.) 10'
    • Application Temperature
    from +10 to +35(°C)
    • Temperature Resistance (after curing)
    -40/+90(°C)

    Packaging
    30/100/250/1000 ml alu bottle;
     

  • u-activator
    Moisture-curing black primer for glass.

    U-Primer 130 is a all-in-one moisture-curing suitable for the application on glass as adhesion promoter and UV barrier as well as paint for bare metal. Before the use shake the bottle for at least one minute and until the sound of the metal spheres inside the bottle is perceived. Once opened and used for a first time, being a product that is highly reactive with moisture, the container must be tightly closed after use. Shake again before any re-use.
  • • Colours Black
    • Solid content 35 %
    • Drying time (23°C and 50% r.h.) 10'
    • Application Temperature
    from +10 to +35(°C)
    • Temperature Resistance (after curing)
    -40/+90(°C)

    Packaging
    30/100/250/1000 ml alu bottle;
     

This site uses cookies to improve the performance of the same . You are free to give your consent to the use of cookies , but , in case of denial , some site functions may not work or have the same performance . For more information on cookies take vision of our privacy policy . To give consent to the use of cookies on this site click the "I accept". Read